Sintering Used Stabilize Zirconia Coating Ceramic Tray Zro2

• Customization: Available
• Application: Refractory, Industrial Ceramic
• Material: Zirconia Ceramic
• Model NO.: YN-L00022
• Process: Industrial Ceramics
• Color: Yellow
• Shape: Board, Plank, Shutter, Plate, Slab, Setter
• Use: Firing Pzt Piezoelectric Parts and Other Electro-C
• Working Temperature: 1600c
• Purtiy: Zro2 and Cao 98.5%, Czo; Zco
• Type: Ceramic Plates
• Transport Package: Pallet
• Specification: CUSTOMIZED
• Trademark: Yunnuo
• Origin: China
• HS Code: 8547100000
• Production Capacity: 500000 PCS/Year
• Package Size: 10.00cm * 10.00cm * 3.00cm
• Package Gross Weight: 0.030kg

Product Description

Product Description

Purity: 98.5% purity
Product process: machine pressing
Color: yellow
Advantages: good thermal shock resistance, high flatness, no slag drop, temperature resistance 1600C

Specification:

Plain flat plate
150x150x6mm
100x100x3.5mm
100x75x3.5mm
Dia 95x4mm

Saggar shape
100x100x13mm
100x100x15mm
115x60x9mm
115x60x7mm
 

Application:
Widely used in ceramic capacitors, sensitive components, magnetic materials, chip inductors and other electronic components industries.

 

These are excellent kiln furniture for firing PZT piezoelectric parts and other electro-ceramics, such as barium titanate (BaTiO3 ) capacitors. DZSP is dimensionally stable to 1650 °C. They are composed of zirconia, partially stabilized with calcia, which is chemically inert and has good thermal shock resistance. It has exceptional resistance to oxidizing and reducing atmospheres at high temperatures. DZSP resists most corrosive environments, and contains no organic binders, produces no smoke and will not outgas.

 

Compositon	ZrO2 + CaO	≥98.5%
	Fe2O3	≤0.1%
	SiO2	≤0.4%
	TiO2	≤0.1%
	Al2O3	≤0.4%
Properties	Apparent porosity	20-29%
	Thermal expansion(1000C)	0.7-0.8%
	Bending Strength	≥20MPa
	Bulk density	4.2-4.6g/Cm3
	Refractoriness under load	≥16500C