Zirconia Setter Plates
Purity: 98.5% purity
Product process: machine pressing
Color: yellow
Advantages: good thermal shock resistance, high flatness, no slag drop, temperature resistance 1600C
Specification:
Plain flat plate
150x150x6mm
100x100x3.5mm
100x75x3.5mm
Dia 95x4mm
Saggar shape
100x100x13mm
100x100x15mm
115x60x9mm
115x60x7mm
Technical Zirconia ceramic plate properties
| Properties |
Unit |
Zirconia Ceramics |
| Composition |
|
Yttria Stabilized |
| Color |
|
Ivory |
| Mechanical |
|
|
| Density |
g/cm3 |
6.05 |
| Youngs Modulus |
GPa |
200 |
| Fracture toughness |
Mpa x m^1/2 |
8 |
| Poissons Ratio |
|
0.30 |
| Compressive Strength |
MPa |
2100 |
| Flexural Strength |
MPa |
850 |
| Hardness (Vickers 500g) |
GPa |
12.5 |
| Thermal |
|
|
| Max Use Temp * |
°C |
1000 |
| Coefficient of Expansion |
10^-6/°C |
10 |
| Thermal Conductivity, 25°C |
W/mK |
2 |
| Thermal Shock Resistance ΔT |
°C |
250 |
| Electrical |
|
|
| Dielectric Strength 6.35mm |
ac-kV/mm |
9.0 |
| Dielectric Constant 25° C |
1 MHz |
29 |
| Volume Resistivity |
|
|
| 25°C |
Ω cm |
>1 x 10^13 |
| 300°C |
Ω cm |
1 x 10^10 |
| 500°C |
Ω cm |
1 x 10^6 |
| 700°C |
Ω cm |
5 x 10 ^3 |
|
Use:
for production of electronic components / Sintering of Electronic Ceramic Components.
Dense Zirconia Setter Plates DZSP are excellent kiln furniture for firing PZT piezoelectric parts and other electro-ceramics, such as barium titanate (BaTiO3 ) capacitors
Application:
Widely used in ceramic capacitors, sensitive components, magnetic materials, chip inductors and other electronic components industries.