| Customization: | Available |
|---|---|
| Application: | Refractory, Industrial Ceramics |
| Grain Size: | 1-10um |
|
Still deciding? Get samples of US$ 50/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
1. The material: Magnesium oxide (Mgo) partially stabilized zirconia (Zro2), Mg-PSZ
2. Property:very high heat-resistant temperature, can be used at temperatures up to 2000°C and has good thermal shock stability,and the product has relatively good mechanical properties. It has excellent chemical stability. Except for sulfuric acid and hydrofluoric acid, it has good stability to acid, alkali and alkali melting, glass melting and molten metal, especially it is not wet with most molten metals. For example, only this material can resist the erosion of molten titanium.
3. It has excellent fire resistance, the maximum use temperature in the air can reach 2200°C, and it can be stable for a long time in a hydrothermal environment, without the problems of low temperature aging. The specific heat and chemical resistance are as follows:
(1.) It has excellent thermal resistance to corrosion in NaOH solution;
(2.) It can resist the corrosion of HCl and H3PO4;
(3.) It can resist the
Textile ceramics are mainly produced from alumina ceramic materials, which have excellent comprehensive technical properties such as high mechanical strength, high hardness, low high-frequency dielectric loss, high temperature insulation resistance, chemical resistance and good thermal conductivity.
Material option:
Steatite
Alumina up to 99.7 % or 95% alumina
Titania
Zirconia
Range of products:
Flange Eyelet, Double flange eyelet, Slotted eyelet, groove eyelets, step eyelet, Cut Eyelet, Step Eyelets, Tubes, Rods, Sleeve,
Ring, Bush, Disc, Dish, Washer, Plates Trap Guide, Traverse Guide, Pig tail Guide, Dog tail Guide, Rollers, Oilers, Oiling Nozzles Cutters
Application :
Yarn manufacturing machines
Twister machines
Airjet looms
Circular looms
weaving machines
winder machines
Rope,Tap plants
Customized guides as per detailed drawings and specifications.
| Item | Unit | 95% al2o3 | 99% al2o3 | Zirconia | Black Tio2 | Yellow Tio2 |
| Color | white,pink | cream,pink | white,black,yellow | Black | Yellow | |
| Density | g/cm3 | 3.65 | 3.9 | 6 | 4 | 4 |
| Flexural strength | MPA | 290 | 390 | 1300 | 70 | 70 |
| Compressive strength | MPA | 3300 | 3900 | 3000 | 600 | 600 |
| Vickers hardness | HV0.5 | 1800 | 2000 | 1150 | 900 | 900 |
| Thermal expansion cofficient | 10-6 K-3 | 5-8.3 | 5.4-8.3 | 10 | 8.5 | 8.5 |
| Thermal conductivity | w/mk | 23 | 28 | 2 | 25 | 25 |